Thienothienylazoanilines in nonlinear optics

ABSTRACT

Use of azo dyes having a diazo component derived from an aminothienothiophene and a coupling component of the aniline series in nonlinear optics, polymers derived from these azo dyes, the use thereof in nonlinear optics, and novel phenylthienothienylazoanilines.

This application is a 371 of PCT/EP44/03685 filed on Nov. 9, 1994.

DESCRIPTION

The present invention relates to the use in nonlinear optics of azo dyes having a diazo component derived from an aminothienothiophene and a coupling component of the aniline series, to polymers derived from these azo dyes, to the use thereof in nonlinear optics, and to novel phenylthienothienylazoanilines.

The nonlinear optical properties of organic compounds find application in many areas of optoelectronics. Examples are applications in frequency doubling, phase modulators, optical amplifiers, interferometers, optical switches or communications technology.

It is common knowledge that organic materials, in particular polymers with certain chromophores, can have nonlinear optical properties which are in some instances more considerable than those of comparable inorganic materials. The materials currently used most frequently are inorganic crystals, for example of potassium dihydrogenphosphate or lithium niobate. These crystals are complicated and costly to produce and, owing to their rigid structure, difficult to use in optical equipment. A further disadvantage is the smallness of their nonlinear effects.

A particular advantage of suitable organic chromophores and their use in polymeric materials is their simple preparation and processing.

The chromophores used in nonlinear optics are generally used either in crystalline form or in polymer-bound form.

Angew. Chem. 96 (1984), 637-651, discloses the use of stilbene derivatives or specific azo dyes for this purpose.

It is an object of the present invention to provide suitable thienothienylazo dyes which are advantageous for use in polymeric nonlinear optical systems. More particularly, such azo compounds shall have large hyperpolarizability values, good thermal stability, good compatibility with the polymers used in nonlinear optical systems, and good film-forming properties with copolymers.

We have found that this object is achieved by azo dyes of the formula I ##STR1## where the ring A may be benzofused,

L¹ and L² are each independently of the other hydrogen, unsubstituted or phenyl-, hydroxyl-, acryloyloxy- or methacryloyloxy-substituted C₁ -C₁₀ -alkyl, or phenyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl, piperidinyl, morpholinyl, piperazinyl or N-(C₁ -C₄ -alkyl)piperazinyl,

L³ and L⁴ are each independently of the other hydrogen, C₁ -C₁₀ -alkyl, C₅ -C₇ -cycloalkyl, C₁ -C₁₀ -alkoxy, cyano or halogen,

R¹ is hydrogen, halogen, nitro, hydroxysulfonyl, formyl, cyano, carbamoyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³, CH═C(NO₂)--X⁴ or ##STR2## where X¹ and X² are each independently of the other C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl or phenyl, X³ is hydroxyl or phenylamino, X⁴ is hydrogen or C₁ -C₄ -alkyl, and X⁵ is hydrogen, nitro, hydroxysulfonyl, formyl, cyano, C₁ -C₄ -alkylsulfonyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³ or CH═C(NO₂)--X⁴, where X¹, X², X³ and X⁴ are each as defined above, and the ring A and L³ and L⁴ are each as defined above,

R² is hydrogen, nitro, cyano, carboxyl or a radical of the formula COX¹, COOX¹ or CONX¹ X², where X¹ and X² are each as defined above, and

R³ is hydrogen, C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl, phenyl or C₁ -C₁₀ -alkoxy,

in that they are advantageous for use in nonlinear optics.

Any alkyl appearing in the abovementioned formula I may be straight-chain or branched.

In substituted alkyl appearing in the abovementioned formula I the number of substituents is generally 1 or 2.

L¹, L², L³, L⁴, X¹, X², X⁴ and R³ are each for example methyl, ethyl, propyl, isopropyl, butyl, isobutyl or sec-butyl.

L¹, L², L³, L⁴, X¹, X² and R³ may each also be for example pentyl, isopentyl, neopentyl, tert-pentyl, hexyl, 2-methylpentyl, heptyl, octyl, 2-ethylhexyl, isooctyl, nonyl, isononyl, decyl or isodecyl (the above designations isooctyl, isononyl and isodecyl are trivial names derived from the oxo process alcohols--cf. Ullmanns Encyklopadie der technischen Chemie, 4th edition, volume 7, pages 215 to 217, and volume 11, pages 435 and 436).

L³, L⁴ and R³ may each also be for example cyclopentyl, cyclohexyl, cycloheptyl, methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, sec-butoxy, pentyloxy, isopentyloxy, neopentyloxy, tert-pentyloxy, hexyloxy, 2-methylpentyloxy, heptyloxy, octyloxy, 2-ethylhexylexy, isooctyloxy, nonyloxy, isononyloxy, decyloxy or isodecyloxy.

L¹, L² and R³ may each also be for example benzyl or 1- or 2-phenylethyl.

L¹ and L² may each also be for example 2-hydroxyethyl, 2- or 3-hydroxypropyl, 2- or 4-hydroxybutyl, 5-hydroxypentyl, 6-hydroxyhexyl, 7-hydroxyheptyl, 8-hydroxyoctyl, 9-hydroxynonyl, 10-hydroxydecyl, 2-acryloyloxyethyl, 2-methacryloyloxyethyl, 2- or 3-acryloyloxypropyl, 2- or 3-methacryloyloxypropyl, 2- or 4-acryloyloxybutyl, 2- or 4-methacryloyloxybutyl, 5-acryloyloxypentyl, 5-methacryloyloxypentyl, 6-acryloyloxyhexyl, 6-methacryloyloxyhexyl, 7-acryloyloxyheptyl, 7-methacryloyloxyheptyl, 8-acryloyloxyoctyl, 8-methacryloyloxyoctyl, 9-acryloyloxynonyl, 9-methacryloyloxynonyl, 10-acryloyloxydecyl or 10-methacryloyloxydecyl.

L³ and L⁴ may each also be for example fluorine, chlorine, bromine or iodine.

X⁵ is for example methylsulfonyl, ethylsulfonyl, propylsulfonyl, isopropylsulfonyl, butylsulfonyl, isobutylsulfonyl or sec-butylsulfonyl.

Preference is given to the use according to the invention of azo dyes of the formula I where L¹ and L² are each independently of the other C₁ -C₄ -alkyl, C₂ -C₈ -hydroxyalkyl, C₂ -C₈ -acryloyloxyalkyl or C₂ -C₈ -methacryloyloxyalkyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl or piperidinyl.

Preference is further given to the use according to the invention of azo dyes of the formula I where L³ and L⁴ are each hydrogen.

Preference is further given to the use according to the invention of azo dyes of the formula I where the ring A is nonbenzofused.

Preference is further given to the use according to the invention of azo dyes of the formula I where R¹ is C₁ -C₆ -alkoxycarbonyl, formyl, acetyl, dicyanovinyl or a radical of the formula ##STR3## wherein X⁵ is as defined above, especially hydrogen, nitro, formyl, cyano, methylsulfonyl or dicyanovinyl, R² is cyano and R³ is hydrogen.

Dicyanovinyl is in particular 2,2-dicyanovinyl.

The azo dyes of the formula I are partly known and described for example in U.S. Pat. No. 4,843,153.

The present invention further provides azo dyes of the formula Ia ##STR4## where the ring A may be benzofused,

L¹ and L² are each independently of the other hydrogen, unsubstituted or phenyl-, hydroxyl-, acryloyloxy- or methacryloyloxy-substituted C₁ -C₁₀ -alkyl, or phenyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl, piperidinyl, morpholinyl, piperazinyl or N-(C₁ -C₄ -alkyl)piperazinyl,

L³ and L⁴ are each independently of the other hydrogen, C₁ -C₁₀ -alkyl, C₅ -C₇ -cycloalkyl, C₁ -C₁₀ -alkoxy, cyano or halogen,

X⁵ is hydrogen, nitro, hydroxysulfonyl, formyl, cyano, C₁ -C₄ -alkylsulfonyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³ or CH═C(NO₂)--X⁴, wherein X¹ and X² are each independently of the other C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl or phenyl, X³ is hydroxyl or phenylamino and X⁴ is hydrogen or C₁ -C₄ -alkyl,

R² is hydrogen, nitro, cyano, carboxyl or a radical of the formula COX¹, COOX¹ or CONX¹ X², where X¹ and X² are each as defined above, and

R³ is hydrogen, C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl, phenyl or C₁ -C₁₀ -alkoxy.

Preference is given to azo dyes of the formula Ia where L¹ and L² are each independently of the other C₁ -C₄ -alkyl, C₂ -C₈ -hydroxyalkyl, C₂ -C₈ -acryloyloxyalkyl or C₂ -C₈ -methacryloyloxyalkyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl or piperidinyl.

Preference is further given to azo dyes of the formula Ia where L³ and L⁴ are each hydrogen.

Preference is further given to azo dyes of the formula Ia where the ring A is nonbenzofused.

Preference is further given to azo dyes of the formula Ia where X⁵ is hydrogen, nitro, formyl, cyano, methylsulfonyl or dicyanovinyl, in particular cyano, R² is cyano and R³ is hydrogen.

The azo dyes of the formula I can be prepared in a conventional manner, for example by diazotizing an amine of the formula II ##STR5## where the ring A, L³, L⁴, X⁵, R² and R³ are each as defined above, and coupling the resulting diazonium compound with a coupling component of the formula III ##STR6## where the ring A, L¹, L², L³ and L⁴ are each as defined above.

The present invention further provides azo dye polymers containing as characteristic monomer units a bivalent radical derived from an azo dye of the formula I and also radicals of the formulae IV, V and VI ##STR7## where Q¹ is hydroxyl, C₁ -C₆ -alkoxy, oxiranylmethoxy, phenoxy, amino or mono- or di(C₁ -C₄ -alkyl)amino,

Q² is hydrogen or methyl, and

W is C₂ -C₁₀ -alkylene,

wherein the proportion of the monomer units of the bivalent radicals derived from the formula I is from 1 to 100 mol %, that of those of the formula IV from 0 to 99 mol %, that of those of the formula V from 0 to 99 mol % and that of those of the formula VI from 0 to 75 mol %, in each case based on the polymer, the average molecular weight of the polymer being from 1000 to 500,000.

Preferably a bivalent radical derived from an azo dye of the formula I conforms to the formula VII ##STR8## where Y is C₂ -C₁₀ -alkylene and the ring A, L², L³, L⁴, R¹, R² and Q² are each as defined above.

The novel polymers can be prepared by methods known per se, as described for example in J. Polymer Sci., Part A, Polymer Chem. 28 (1990), 1-13.

Advantageously an appropriate azo dye of the formula I is reacted with an acryloyl compound of the formula VIII ##STR9## where Q¹ and Q² are each as defined above, styrene and a cinnamic ester of the formula IX ##STR10## where Q² and W are each as defined above, in the abovementioned molar ratio in an inert solvent (eg. toluene or xylene) in the presence of a free radical initiator (eg. azobisisobutyronitrile).

The polymers containing azo dyes of the formula I are advantageously suitable for use in nonlinear optics.

The compounds of the invention are thermally stable and have particularly large molecular hyperpolarizability values (β). In addition, the dyes are highly compatible with the polymers used in nonlinear optical systems and have good film-forming properties in copolymers.

The molecular hyperpolarizability can be determined for example by the method of solvatochromism (see for example Z. Naturforschung 20a (1965), 1441-1471, or J. Org. Chem. 54 (1989), 3775-3778). This method of measurement involves determining the position of the absorption band of a compound in different solvents, for example in dioxane or dimethyl sulfoxide. The shift of the absorption band is then directly proportional to the β value, ie. compounds having a large solvatochromic shift have a large molecular hyperpolarizability and are therefore highly suitable for use in nonlinear optical systems (see for example Chemistry and Industry, 1990, pages 600 to 608).

Of particular note is the suitability of the novel substances for use in communications technology, electrooptical modulators (eg. Mach-Zehnder interferometers), optical switches, frequency mixing or waveguides.

The Examples which follow illustrate the invention.

EXAMPLE 1

1.0 g (0.004 mol) of the compound of the formula ##STR11## (prepared as described in Example 3 of U.S. Pat. No. 4,843,153) was suspended at 0°-5° C. in 20 ml of 17:3 v/v glacial acetic acid/propionic acid and admixed with 1.6 g of nitrosylsulfuric acid. After stirring at 5° C. for 1 h the resulting solution was added to a mixture of 0.65 g (0.004 mol) of N,N-diethylaniline in 5 ml of 17:3 v/v glacial acetic acid/propionic acid. The mixture was stirred for 30 min and then poured onto 250 ml of ice-water. The mixture was filtered with suction and the filter residue was washed with water. Drying under reduced pressure at 50° C. left 1.2 g of a red dye of the formula ##STR12##

EXAMPLE 2

1.0 g (0.004 mol) of the compound of the formula ##STR13## was suspended at 0°-5° C. in 20 ml of 17:3 v/v glacial acetic acid/propionic acid and admixed with 1.6 g of nitrosylsulfuric acid. After stirring at 5° C. for 1 h the resulting solution was added to a mixture of 0.65 g (0.004 mol) of N-phenylpyrrolidine and 5 ml of 17:3 v/v glacial acetic acid/propionic acid. The mixture was stirred for 30 min at 0° to 5° C. and then poured onto 250 ml of ice-water. The mixture was filtered with suction and the filter residue was washed with 1 l of water. Drying under reduced pressure at 50° C. left 1.13 g of a red dye of the formula ##STR14##

EXAMPLE 3

1.0 g (0.004 mol) of the compound of the formula ##STR15## was suspended at 0°-5° C in 20 ml of 17:3 v/v glacial acetic acid/propionic acid and admixed with 1.16 g of nitrosylsulfuric acid. After stirring at 5° C. for 1 h the resulting solution was added to a mixture of 1.088 g (0.004 mol) of the compound of the formula ##STR16## and 5 ml of 17:3 v/v glacial acetic acid/propionic acid. The mixture was stirred at 0°-5° C. for 30 min and then poured onto 250 ml of ice-water. The mixture was filtered off with suction and the filter residue was washed with 1 l of water. Drying under reduced pressure left 1.92 g of a dye of the formula ##STR17##

EXAMPLE 4

a) 73.15 g (0.21 mol) of the compound of the formula ##STR18## were heated in 370 ml of N,N-dimethylformamide at 100° C. for 7 h together with 25.5 g (0.33 mol) of sodium acetate. The resulting precipitate was then filtered off with suction, washed with water and dried at 50° C. under reduced pressure to yield 24.6 g of the compound of the formula ##STR19##

mp.: 243°-244° C. Analysis: calc C 67.08 H 3.97 N 18.41 S 10.53 found C 67.14 H 4.04 N 17.88 S 10.38

b) 7.8 g (0.023 mol) of the compound described in Example 4a were heated in 40 ml of N-methylpyrrolidone at 100° C. for 2 h in the presence of 4.6 g of concentrated hydrochloric acid. The reaction batch was then precipitated onto 500 g of ice-water, and the precipitate was filtered off with suction, washed with 200 ml of water and dried at 50° C. under reduced pressure to yield 6.6 g of a compound of the formula ##STR20##

c) 4.78 g (0.017 mol) of the compound described in Example 4b were admixed at 0°-5° C. in 170 ml of 17:3 v/v glacial acetic acid/propionic acid with 5.34 g of nitrosylsulfuric acid. After subsequent stirring at 0°-5° C. for 2 h, 2.94 g (0.0187) of N-ethyl-N-(2-hydroxyethyl)aniline were added in the cold. After 2 h the precipitate was filtered off with suction, washed with water and dried under reduced pressure to yield 5.0 g of a dye of the formula ##STR21##

mp.: 272°-273° C. Analysis: calc C 63.00 H 4.19 O 3.5 N 15.31 S 14.01 found C 63.20 H 4.20 O 3.8 N 14.90 S 13.90

The same method produces the following compounds:

    __________________________________________________________________________     Ex. No.                                                                        __________________________________________________________________________          ##STR22##                                                                 6                                                                                   ##STR23##                                                                 7                                                                                   ##STR24##                                                                 8                                                                                   ##STR25##                                                                 __________________________________________________________________________

The method described in Z. Naturforschung 20a (1965), 1441-1471, was employed to measure the absorption maximum of the individual dyes in both dioxane and dimethyl sulfoxide (DMSO) and then to determine the solvatochromic shift Δ_(v) cm⁻¹ !.

The respective results are listed in the following table:

                  TABLE                                                            ______________________________________                                                           λ.sub.max                                                                           λ.sub.max                                                   (dioxane)   (DMSO) Δv                                  Ex. No.  Dye No.   nm!         nm!    cm.sup.-1 !                              ______________________________________                                          9       1        550         583    1029                                      10       2        552         591    1195                                      11       3        558         590     972                                      12       4        568         595     799                                      ______________________________________                                     

We claim:
 1. In a nonlinear optical system, the improvement comprising using an azo dye of the formula I ##STR26## where the ring A may be benzofused,L¹ and L² are each independently of the other hydrogen, unsubstituted or phenyl-, hydroxyl-, acryloyloxy- or methacryloyloxy-substituted C₁ -C₁₀ -alkyl, or phenyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl, piperidinyl, morpholinyl, piperazinyl or N-(C₁ -C₄ -alkyl)piperazinyl, L³ and L⁴ are each independently of the other hydrogen, C₁ -C₁₀ -alkyl, C₅ -C₇ -cycloalkyl, C₁ -C₁₀ -alkoxy, cyano or halogen, R¹ is hydrogen, nitro, hydroxysulfonyl, carbamoyl, dicyanovinyl or a radical of the formula CONX¹ X², CH═N--X³, CH═C(NO₂)--X⁴ or ##STR27## where X¹ and X² are each independently of the other C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl or phenyl, X³ is hydroxyl or phenylamino, X⁴ is hydrogen or C₁ -C₄ -alkyl, and X⁵ is hydrogen, nitro, hydroxysulfonyl, formyl, cyano, C₁ -C₄ -alkyl-sulfonyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³ or CH═C(NO₂)--X⁴, where X¹, X², X³ and X⁴ are each as defined above, and the ring A and L³ and L⁴ are each as defined above, R² is hydrogen, nitro, cyano, carboxyl or a radical of the formula COX¹, COOX¹ OR CONX¹ X², where X¹ and X² are each as defined above, and R³ is hydrogen, C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl, phenyl or C₁ -C₁₀ -alkoxy.
 2. The nonlinear optical system as claimed in claim 1, wherefor L¹ and L² are each independently of the other C₁ -C₄ -alkyl, C₂ -C₈ -hydroxyalkyl, C₂ -C₈ -acryloyloxyalkyl or C₂ -C₈ -methacryloyloxyalkyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl or piperidinyl.
 3. The nonlinear optical system as claimed in claim 1, wherefor L³ and L⁴ are each hydrogen.
 4. The nonlinear optical system as claimed in claim 1, wherefor R¹ is dicyanovinyl or a radical of the formula ##STR28## wherein X⁵ is as defined in claim 1, R² is cyano and R³ is hydrogen.
 5. An azo dye of the formula Ia ##STR29## where the ring A may be benzofused,L¹ and L² are each independently of the other hydrogen, unsubstituted or phenyl-, hydroxyl-, acryloyloxy- or methacryloyloxy-substituted C₁ -C₁₀ -alkyl, or phenyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl, piperidinyl, morpholinyl, piperazinyl or N-(C₁ -C₄ -alkyl)piperazinyl, L³ and L⁴ are each independently of the other hydrogen, C₁ -C₁₀ -alkyl, C₅ -C₇ -cycloalkyl, C₁ -C₁₀ -alkoxy, cyano or halogen, X⁵ is hydrogen, nitro, hydroxysulfonyl, formyl, cyano, C₁ -C₄ -alkylsulfonyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³ or CH═C(NO₂)--X⁴, wherein X¹ and X² are each independently of the other C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl or phenyl, X³ is hydroxyl or phenylamino and X⁴ is hydrogen or C₁ -C₄ -alkyl, R² is hydrogen, nitro, cyano, carboxyl or a radical of the formula COX¹, COOX¹ or CONX¹ X², where X¹ and X² are each as defined above, and R³ is hydrogen, C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl, phenyl or C₁ -C₁₀ -alkoxy.
 6. The azo dye as claimed in claim 5, wherein L¹ and L² are each independently of the other C₁ -C₄ -alkyl, C₂ -C₈ -hydroxyalkyl, C₂ -C₈ -acryloyloxyalkyl or C₂ -C₈ -methacryloyloxyalkyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl or piperidinyl.
 7. The azo dye as claimed in claim 5, wherein L³ and L⁴ are each hydrogen.
 8. The azo dye as claimed in claim 5, wherein X⁵ is hydrogen, nitro, formyl, cyano, methylsulfonyl or dicyanovinyl, R² is cyano and R³ is hydrogen.
 9. In a nonlinear optical system, the improvement comprising using the azo dye polymer of claim
 10. 10. An azo dye polymer containing as characteristic monomer units a bivalent radical derived from an azo dye of the formula I ##STR30## where the ring A may be benzofused,L¹ and L² are each independently of the other hydrogen, unsubstituted or phenyl-, hydroxyl-, acryloyloxy- or methacryloyloxy-substituted C₁ -C₁₀ -alkyl, or phenyl, or L¹ and L² are together with the nitrogen atom joining them together pyrrolidinyl, piperidinyl, morpholinyl, piperazinyl or N-(C₁ -C₄ -alkyl)piperazinyl, L³ and L⁴ are each independently of the other hydrogen, C₁ -C₁₀ -alkyl, C₅ -C₇ -cycloalkyl, C₁ -C₁₀ -alkoxy, cyano or halogen, R¹ is hydrogen, nitro, hydroxysulfonyl, carbamoyl, dicyanovinyl or a radical of the formula CONX¹ X², CH═N--X³, CH═C(NO₂)--X⁴ or ##STR31## where X¹ and X² are each independently of the other C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl or phenyl, X³ is hydroxyl or phenylamino, X⁴ is hydrogen or C₁ -C₄ -alkyl, and X⁵ is hydrogen, nitro, hydroxysulfonyl, formyl, cyano, C₁ -C₄ -alkyl-sulfonyl, dicyanovinyl or a radical of the formula COX¹, COOX¹, CONX¹ X², CH═N--X³ or CH═C(NO₂)--X⁴, where X¹, X², X³ and X⁴ are each as defined above, and the ring A and L³ and L⁴ are each as defined above, R² is hydrogen, nitro, cyano, carboxyl or a radical of the formula COX¹, COOX¹ OR CONX¹ X², where X¹ and X² are each as defined above, and R³ is hydrogen, C₁ -C₁₀ -alkyl, which may be phenyl-substituted, C₅ -C₇ -cycloalkyl, phenyl or C₁ -C₁₀ -alkoxy,and also radicals of the formulae IV, V and VI ##STR32## where Q¹ is hydroxyl, C₁ -C₆ -alkoxy, oxiranylmethoxy, phenoxy, amino or mono- or di(C₁ -C₄ -alkyl)amino, Q² is hydrogen or methyl, and W is C₂ -C₁₀ -alkylene,wherein the proportion of the monomer units of the bivalent radicals derived from the formula I is from 1 to 100 mol %, that of those of the formula IV from 0 to 99 mol %, that of those of the formula V from 0 to 99 mol % and that of those of the formula VI from 0 to 75 mol %, in each case based on the polymer, the average molecular weight of the polymer being from 1000 to 500,000. 